Effect of substrate temperature on the resistance to wear for Nitec coatings deposited via thermal flame-spraying technique

Vista sencilla de ítem
dc.contributor.authorOtálora Sánchez, Diego Fernando
dc.date2015-12-01
dc.descriptionResults for the deposition of nickel-based coatings on iron substrates using the thermal flame-spraying technique, with surface preparation by sand blasting, are presented. Basically, we studied the influence of the temperature of the substrate on the structural, morphological, and wear resistance properties. The coatings were structurally characterized via X-ray diffraction (XRD), and the surface morphology was characterized through scanning electron microscopy (SEM) and confocal laser microscopy (MLC). The chemical composition was determined by means of Xray fluorescence (XRF), and wear was evaluated by testing three-body abrasive wear, ball-on-disk and scratch tester. Through XRD results, it was established that the coatings are polycrystalline and have a bodycentered cubic (BCC) crystal structure at all deposition temperatures. SEM analysis determined that the surfaces of the films decrease their porosity as the deposit temperature increases, and wear tests showed that the coatings are more resistant to this test than is the substrate.en-US
dc.descriptionEn este trabajo se presentan los resultados obtenidos en el depósito de recubrimientos a base de níquel sobre sustratos de hierro, con preparación de superficie mediante granallado por arena, utilizando la técnica de proyección térmica por llama. Básicamente, se estudió la influencia que tiene la temperatura de depósito del sustrato sobre las propiedades estructurales, morfológicas y en la resistencia al desgaste. Los recubrimientos fueron caracterizados estructuralmente mediante difracción de rayos X (DRX); la morfología de la superficie se caracterizó mediante microscopía electrónica de barrido (MEB) y microscopia laser confocal (MLC). La composición química se determinó mediante fluorescencia de rayos X (FRX) y la respuesta al desgaste se evaluó mediante pruebas de desgaste abrasivo a tres cuerpos, bola sobre disco y rayado. Los resultados de DRX permitieron establecer que los recubrimientos son policristalinos y tienen una estructura cristalográfica cubica centrada en el cuerpo (BCC) para todas las temperaturas de depósito; el análisis de MEB determino que las superficies de las películas disminuyen su porosidad a medida que la temperatura de depósito aumenta y las pruebas de desgaste mostraron que los recubrimientos son más resistentes a ésta prueba que el sustrato.es-ES
dc.formatapplication/pdf
dc.identifierhttps://revistas.unilibre.edu.co/index.php/avances/article/view/267
dc.identifier10.18041/1794-4953/avances.2.267
dc.identifier.urihttp://hdl.handle.net/10901/15077
dc.languagespa
dc.language.isospaspa
dc.publisherUniversidad Librees-ES
dc.relationhttps://revistas.unilibre.edu.co/index.php/avances/article/view/267/213
dc.relation/*ref*/Y. B. W. S.-C. K. Y.-J. J., M. Han. (2008). Effects ofthickness of al thermal spray coating for STS 304.Jun.
dc.relation/*ref*/Dimaté, C. L. (2011) Resistencia a la corrosión enrecubrimientos comerciales metaceram 25050 y proxon21071 producidos con el sistema de proyección térmica porllama. Tesis de maestría.
dc.relation/*ref*/Galvele, J. R., Gustavo, S. D. (2006). Degradaciónde materiales (1ra ed.). Buenos Aires: Jorge Baudinoeditores.
dc.relation/*ref*/CSM., I. (2009). Characterization of thermal spraycoatings by instrumented indentation and scratchtesting. Applications Bulletin., Part I, No. 28. Abril.
dc.relation/*ref*/Lucena, J. (2008). Análisis de falla de piezas de laindustria naval que pueden ser recuperadas por técnicas deproyección térmica. Trabajo de grado.
dc.relation/*ref*/Siegmann, S., C. A. (2013). 100 years of thermalspray: About the inventor Max Ulrich Schoop.Surface & Coatings Technology, pp. 3-13.
dc.relation/*ref*/Fang, L., Zhou, Q. (1998). An experimentalsimulation of cutting wear three body-abrasion.Department of science and engineering”. HarbinInstitute of Technology, vol. 219, pp. 188-194.
dc.relation/*ref*/Premachandran, N. (2009). The use of the pin-ondisktribology test method to study three uniqueindustrial applications. 17th International Conference onWear of Materials, 267, pp. 823-827.
dc.relation/*ref*/Davis, J. R. (2004). Handbook of thermal spraytechnology. ASM International. ISBN 0-87170-795-0,pp. 329.
dc.relation/*ref*/Marulanda, J. (2007). Protección contra la corrosión pormedio del rociado térmico. Trabajo de grado.
dc.relation/*ref*/ASTM. (2005). Standard test method for weartesting with a pin-on-disk apparatus. G99 – 05.
dc.relation/*ref*/ASTM. (2008). Standard C633 − Standard testmethod for adhesion or cohesion strength ofthermal spray coatings reapproved.
dc.relation/*ref*/Jahromi, S. P. (2012). Facile synthesis of porousstructurednickel oxide thin film by pulsed laserdeposition. 13 September.
dc.relation/*ref*/Saw, K. G. (2014). Ohmic-rectifying conversion ofNi contacts on ZnO and the possible determinationof ZnO thin film surface polarity. Published onlineJan 23.
dc.relation/*ref*/Martínez, G. (2013). Resistencia a la corrosión derecubrimientos nitec y metaceram 23075depositados mediante la técnica de proyeccióntérmica por llama para la industria naval.
dc.relation.ispartofjournalRevistas – Ingenieríasspa
dc.rights.licenseAtribución-NoComercial-SinDerivadas 2.5 Colombia*
dc.rights.urihttp://creativecommons.org/licenses/by-nc-nd/2.5/co/*
dc.sourceAvances: Investigación en Ingeniería; Vol 12 No 1 (2015): Avances Investigación en Ingenieríaen-US
dc.sourceAvances: Investigación en Ingeniería; Vol. 12 Núm. 1 (2015): Avances Investigación en Ingenieríaes-ES
dc.source2619-6581
dc.source1794-4953
dc.subject.proposalRevestimientos protectoresspa
dc.subject.proposalGranalladospa
dc.subject.proposalIngeniería industrialspa
dc.titleEffect of substrate temperature on the resistance to wear for Nitec coatings deposited via thermal flame-spraying techniqueen-US
dc.titleEfecto de la temperatura del sustrato sobre la resistencia al desgaste de recubrimientos de Nitec depositados utilizando la técnica de proyección térmica con llamaes-ES
dc.type.coarhttp://purl.org/coar/resource_type/c_6501
dc.type.coarversionhttp://purl.org/coar/version/c_970fb48d4fbd8a85
dc.type.localPeer reviewed Articleen-US

Archivos

Colecciones

Avances: Investigación en Ingeniería